A LLDPE-Based XLPE Insulation Material Using BIPB as Crosslinking Agent
ID：542
View Protection：ATTENDEE
Updated Time：2022-09-16 20:52:55
Hits：346
Poster Presentation
Start Time：Pending（Asia/Shanghai）
Duration：Pending
Session：No Session »
Video
No Permission
Presentation File
Tips: Only the registered participant can access the file. Please sign in first.
Abstract
In this paper, a different type of cross-linking agent, bis (1- (tert-butylperoxy)-1-methylethyl)-benzene (BIPB), was investigated for XLPE insulation. In order to explore its cross-linking effect and the difference on the performance of XLPE between using BIPB and DCP (Dicumyl peroxide) as crosslinking agent, with the linear-low-density polyethylene (LLDPE) as base material, the relationship between the content of BIPB on the gel content was established, and the effects of the gel content on the crystallinity and DC breakdown characteristics of XLPE as well as its mechanical properties were further compared. The experimental results shows that the performance of XLPE under similar gel content using different crosslinking agent is similar. It can be concluded that with the increase of peroxide content, the gel content of the samples is increasing, which can represent the increase of the crosslinking degree of XLPE. And the crystallinity of XLPE decrease with the increase of gel content, and its DC breakdown strength increases with the increase of crosslinking degree under 70℃. What’s more, both crystallinity and crosslinking degree affect the mechanical properties of XLPE, which leads to the change of tensile strength and elongation at break. It can be found that it only costs about 3/5 of DCP content to achieve the similar crosslinking effect for BIPB, that is, the crosslinking efficiency of BIPB is better.
Keywords
XLPE Cable;bipb;dcp;Crosslinking
Speaker
Xiangchen Liu
State Key Laboratory of Electrical Insulation and Power Equipment；Xi'An Jiaotong UniversitySubmission Author
All Comments
Important Date
-
Conference Date
Sep 25
2022
toSep 29
2022
-
Aug 15 2022
Early Bird Registration
-
Sep 10 2022
Contribution Submission Deadline
-
Nov 10 2022
Registration deadline
-
Nov 30 2022
Draft paper submission deadline
-
Nov 30 2022
Final Paper Deadline
Sponsored By
IEEE DEIS
Organized By
Chongqing University
Contact Information
- Zhengyong Huang
- 61******@qq.com
Previous Conferences
-
2020-09-06 China Beijing
2020 IEEE International Conference on High Voltage Engineering and Application -
2018-09-10 Greece
2018 IEEE International Conference on High Voltage Engineering and Application -
2016-09-19 China Chengdu, China
2016 IEEE International Conference on High Voltage Engineering and Application
Submit Comment